User manual 3M SCOTCH-WELD PUR ADHESIVE SYSTEM BROCHURE

[. . . ] Helps simplify production as well as save energy. A C 2 4 · 100% solids gives you a low-VOC adhesive system with no drying equipment and no attack on plastics. Structural strength · Up to a half ton in holding power after only ten minutes exceeds strength of conventional hot melt and PVA adhesives. B · Eliminates nails and other mechanical fasteners in many applications to help save the time of finishing steps. Application versatility · Proprietary chemistry bonds a wide variety of substrates, including wood, plastics, rubber, dissimilar materials and plasticized vinyls. · Up to 10-minute open time allows positioning of multiple or complex parts. · Thin, flexible and tough bond lines help improve the fit, appearance and durability of your product. · Help you meet production volume requirements with self-contained hand-held Jet-Weld II Applicator or your own bulk dispensing equipment. 3 Photo courtesy of David Trubridge designer. Application ideas · Countertop edging (A) ­ Adhesive bead applies neatly and eliminates nails and the extra work of putty and sanding. [. . . ] See data sheets for additional technical information about 3M Jet-Weld Adhesives. 0 psi 5 min Jet-Weld Adhesive 10 min PVA 15 min 30 min 2-Part Epoxy 1 hr 2 hr Hot Melt (C) 3MTM Jet-WeldTM Adhesive speed decreases fixture time to help increase productivity. In only 10 minutes, bond strength exceeds the structural strength base line of 1, 000 psi in lap shear. After an hour, strength is greater than many substrates (note splice test at right). 13 Note: This technical information and data should be considered representative or typical only and should not be used for specification purposes. eater than many substrates 3MTM Jet-WeldTM Adhesive Information Product TE-015 Description Extrudable. Very fast set time for bonding wood and selected plastics. Best for bonding wood and selected plastics. Fast set for bonding wide variety of plastics, including polystyrene and polyacrylic. Fast set time, low viscosity, and strong, flexible bonds for a wide variety of plastics, wood, aluminum and glass. Medium set time and low viscosity for bonding wood and selected plastics. Long set time for wide variety of plastics, including polystyrene and polyacrylic. Bonds aluminum and glass to plastic and wood. Bonds substrates such as wood, FRP and many other plastics to themselves, metal, and glass. Very high green strength. Application Viscosity Temperature 250°F (121°C) 250°F (121°C) 250°F (121°C) 250°F (121°C) 7, 000 cps 16, 000 cps 13, 000 cps 7000 cps Color White/ off white White/ off white White/ off white White/ off white Open Time 1. 5 min. 40 sec. Shore Tensile Strength D 65 3950 psi 3800 psi 3900 psi 2750 psi Elong. 750% Modulus 2500 psi TE-030 60 725% 11, 200 psi 5600 psi 2850 psi TE-031 50 725% TE-040 35 860% TE-100 250°F (121°C) 250°F (121°C) 7000 cps 3000 cps 9000 cps White/ off white White/ off white White/ off white 2 min. 2. 5 min. 61 4200 psi 4000 psi 675% 12, 200 psi 9700 psi TE-200 60 625% TS-230 250°F (121°C) 45 3300 psi 700% 5400 psi TS-115 HGS 250°F (121°C) 16, 000 cps White/ off white 10 min. 1 min. 47 3200 psi 600% 3300 psi 3MTM Jet-WeldTM Adhesive Selection Guide Substrate ABS Aluminum 1, 2 EPDM rubber Fabric/felt/cork FRP ­ epoxy FRP ­ polyester Glass/ceramic Leather Neoprene rubber 3 Nitrile rubber 3 Nylon Painted metal Polyacrylic Polycarbonate Polyolefins 5 Polystyrene Polystyrene (Beadboard) 4 1 TE-015 TE-030 TE-031 TE-040 TE-100 TE-200 TS-230 TS-115 HGS Excellent Good Fair Poor 1 Not recommended for bonding metal, glass and ceramic to itself or each other due to low moisture transmission of substrates. Not for use on uncoated aluminum subjected to hot/humid conditions. Adhesion to specific rubber must be evaluated by user. 4 Adhesive may partially delaminate from polycarbonate at elevated temperatures. Corona or plasma treatment may improve adhesion. [. . . ] 4) 0. 125" orifice for high flow applications. 0. 090" orifice tip comes standard with the applicator. 19 · Applicator rest holds applicator upright when not in use. Frees both hands for component assembly. · Impact-resistant plastic construction is engineered for lightweight handling ease and the hard realities of the shop and plant. · 100% solids 3MTM Jet-WeldTM Adhesive is applied molten at only 250°F (121°C). No temperature adjustments required. · Open time up to 10 minutes allows product positioning. · Set time as fast as 15 seconds helps eliminate or minimize fixturing. [. . . ]